Truck Flooring
Truck Flooring
A compressed densified composite product based on woodveneer impregnated with phenolic resins product requires very high compressive strength and so structure of the veneer configuration is so designed to get maximum required mechanical properties. Here, resins impregnated veneers are assembled to required pack by putting each veneer one over another at right angles to each other and pressed under high temperature and pressure with the help of high capacity press. The pressed martial is then removed from the pressing system after giving sufficient cooling.
This martial possess following characteristics qualities and are as follows:-
Very high density, less moisture content, less moisture abortion properties, high tensile strength, high bending strength, high compressive strength, very accurate edges straightness, easy to cut any length and width by any heavy duty wood working machines, very high surface hardness coupled with high absorption resistance etc. Further every sheet will have two layers of metal net inserted inside the surface of the material from top and bottom as reinforcement so that the material can carry extra additional weight. Without fracturing the material at any point of its life.
| Additional Info: | |
|---|---|
|
Std. Thickness |
12, 16, 19 & 25 mm |
|
Sizes |
Length : 2440 to 3350 mm Width : 600 to 1820 mm |
|
Density |
0.845 to 1.00 gm/cm3 |
|
Applications |
It can be used in truck, commercial vehicle flooring & other industrial uses. Also in automobile sector deck, ceiling, paneling back rest seat, anti skid flooring etc. |
Technical Specification
| Sr No. | Dimensions | ISI Requirements | Observed Values | |
|---|---|---|---|---|
|
1. |
Length |
2440:+6 0 |
2442mm |
|
|
2. |
Width |
1220:+3 0 |
1222mm |
|
|
3. |
Thickness |
25mm 24.90mm |
|
|
|
4. |
Squareness |
2mm/1000mm |
0.95mm |
|
|
5. |
Edge Straightness |
2mm/1000mm |
0.50mm |
|
|
6. |
Workmanship & Finish |
Satisfactory |
|
|
|
Physical properties |
||||
|
7. |
Density |
0.95 gm/cm² |
0.97 gm/cm² |
|
|
8. |
Moisture Content |
5-15% |
7.90% |
|
|
9. |
Bond Quatlity Test
Boiling - Drying @ 60+_2°c 4 Hrs. - 20 Hrs. Three Cycle |
a) No Visible delamination in glue line and plywood face b) No forcible separation and fibre should be adhered between plies |
Satisfactory |
|
|
10. |
Breaking Strength 250 x 50 x Thickness(mm |
Along - 550kgf Across - 400kgf |
729kgf 493kgf |
|
|
11. |
Static Bending Strength |
|||
|
|
Along the grain M.O.E. |
Avg. - 7500N/mm² Ind. - 6700N/mm² |
8544.35 N/mm² 7353..42 N/mm² |
|
|
|
Across the grain M.O.E. |
Avg. - 4000N/mm² Ind. - 3600N/mm² |
5973.94 N/mm² 4120.30 N/mm² |
|
|
|
Along the grain M.O.R. |
Avg. - 50 Ind. - 45 |
70.224 N/mm² 48.29 N/mm² |
|
|
|
Across the grain M.O.R. |
Avg. - 30 Ind. - 27 |
58.782 N/mm² 42.30 N/mm² |
|
|
12. |
Tensile Strength |
Along - 55 MPa Across - 50 MPa |
68.32 MPa 57.29 MPa |
|