Premium compressed Plywood made up of high strength wood veneers impregnated with phenolic resins. Here each layer of the pack is assembled by keeping each veneer one over other at right angles to each other, pressed under high temperature and pressure and then removed from the pressed system after giving sufficient cooling. It posses high mechanical strength coupled with very low moisture absorption properties. The material is very Flat in nature and possess extra bouncing properties so as to meet required standard characteristic qualities.
Density
0.95 to 1.15 gm/cm3
Std. Thickness (mm)
12 to 80
Standard Sizes (ft)
10.5×5.5, 10×5, 9×5, 8×5, 7×5, 6×5, 5×5
Wood Species
High density hardwood
TT Table Plywood
| Sr No. | Properties | BIS Requirement IS 3513:1989 | Observed Values |
|---|---|---|---|
|
1. |
Length |
2440mm |
2442mm |
|
2. |
Moisture Content Dimesion |
5% - 15% Length +5mm width +2mm thickness ≥ 6mm - ±5%, < 6mm - ± 10% |
8%
Within limit |
|
3. |
Thickness |
12mm |
12.10mm
|
|
4. |
Squareness |
2% |
1mm |
|
5. |
Edge straightness |
2% |
0.95mm |
|
6. |
Density |
0.95 to 1.25 gm/cm2 |
1.00 gm/cm2
|
|
7. |
Moisture content |
6 to 12% |
7.50% |
|
Physical properties |
|||
|
8. |
Tensile strength |
59 Mpa |
142 Mpa |
|
9. |
Static bending MOR |
59 Mpa |
180 Mpa |
|
10. |
Compressive strength parallel to laminate |
75 Mpa |
125 Mpa |
|
11. |
Perpendicular to laminate |
130 Mpa |
175 Mpa |
|
12. |
Hardness test hardness on rockwell H scale |
60 |
65 |
|
13. |
Impact strength parallel to laminate |
0.5 kg-M/cm2 |
0.57 kg-M/cm2 |
|
14. |
Perpendicular to laminate |
0.2 kg-M/cm2 |
0.27 kg-M/cm2 |